Abstract
To evaluate the effect of circular holes on the mechanical properties of laminated composite plates with different sizes, static tensile destructive tests were carried out on four different types of composite laminated plates with different layups and aperture sizes. The experimental results showed that for the four types of layup, the strength of the specimens with a diameter of 6.35 mm decreased by 44.3 %, 51.3 %, 48.0 %, and 39.4 % compared to intact specimens, and the greater the proportion of 0° layup, the greater the strength decrease of the perforated specimens. Under the same layup, as the diameter of the circular hole increased, the tensile strength decreased rapidly with the constant ratio of diameter to width. Based on the experimental results, three commonly used models for predicting the residual strength of perforated laminated composite plates, including point stress criterion, average stress criterion, and stress field intensity method, were evaluated. The results showed that the average stress criterion had higher accuracy compared to the point stress criterion and the stress field intensity method.
Reference16 articles.
1. Z. H. Sun, Y. Tie, L. Cheng, and Y. L. Hou, “Damage analysis experimental study of Open-hole CFRP composite laminates,” (in Chinese), FRP /CM, No. 1, pp. 5–10, 2019.
2. N. B. Yang and Y. N. Zhang, Design of Composite Aircraft Structures. (in Chinese), Aviation Industry Press, 2004.
3. J. M. Whitney and R. J. Nuismer, “Stress fracture criteria for laminated composites containing stress concentrations,” Journal of Composite Materials, Vol. 8, No. 3, pp. 253–265, 1974.
4. R. Nuismer and J. Labor, “Applications of the average stress failure criterion: part I – tension,” Journal of Composite Materials, pp. 238–249, 1978.
5. R. J. Nuismer and J. D. Labor, “Applications of the average stress failure criterion: part II – Compression,” Journal of Composite Materials, Vol. 13, No. 1, pp. 49–60, Jan. 1979, https://doi.org/10.1177/002199837901300104
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献