Optical Properties of Newly Developed Monolithic CAD/CAM Materials After Aging

Author:

UYSAL ÖZEL Hatice Banu1ORCID,ASLAN Yılmaz Umut2ORCID,SANCAKLI Erkan3ORCID

Affiliation:

1. İstanbul Üniversitesi Diş Hekimliği Fakültesi Protetik Diş Tedavisi A.D. Çene Yüz Protezleri Bilim Dalı

2. MARMARA ÜNİVERSİTESİ, DİŞ HEKİMLİĞİ FAKÜLTESİ

3. İSTANBUL ÜNİVERSİTESİ, DİŞ HEKİMLİĞİ FAKÜLTESİ

Abstract

Objective: With the widespread use of CAD/CAM (computer aided design and manufacture) systems in dentistry, many restorative materials have been produced. In our study, we aimed to evaluate the change in optical properties of newly developed translucent monolithic zirconia (TMZ) (Cercon HT Dentsply, Sirona, USA), zirconia-reinforced lithium silicate (ZLS) (Celtra Duo, Dentsply, Germany) and lithium disilicate (LS2) (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein) materials with aging. Methods:10 discs of 12mm diameter and 1.2 mm thickness were produced from high translucent A2 color of each material. The aging process was applied in an autoclave under 134ºC, 0.2MPa pressure. For optical evaluation, L*, a*, b* values of the samples were measured by spectrophotometry before aging, after 3 hours and 6 hours aging. ΔE00 values and translucency parameters (TP) were calculated. The data were evaluated statistically. Results: In the present study, all the materials had undergone color change as a result of aging, but this change was within acceptable limits (ΔE00 0.8). There was a decrease in the translucency of all materials used in the study, but this decrease was not statistically significant. Conclusion: In the light of the findings obtained from this in vitro study, aging did not cause color and translucency changes in TMZ, ZLS, LS2 monolithic CAD/CAM materials.

Funder

İstanbul Üniversitesi Bilimsel Araştırma Projeleri Birimi

Publisher

Marmara University

Subject

General Materials Science

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3