Abstract
The process of forming a composite material carbon-graphite-aluminum by impregnating a porous frame AG-1500 with aluminum melt at a temperature of 650С is studied. The redistribution of elements of the impregnating alloy is established. it is shown that the transition of silicon, Nickel, chromium, and iron from the aluminum melt to the «melt - pore surface of carbon graphite» is determined not by the mechanism of chemical localization of conduction electrons, but by the rearrangement of the electronic structure of components during crystallization. In this case, it is possible to change the solubility of the melt elements in aluminum, as a result of the combined action of pressure and temperature on it during the impregnation process.
Publisher
Volgograd State Technical University
Reference10 articles.
1. Костиков, В. И. Фрикционные свойства углерод-углеродных композиционных материалов / В. И. Костиков, Ж. В. Еремеева, Д. А. Слюта, Д. Л. Яицкий, Г. Х. Шарипзянова // Известия вузов. Порошковая металлургия. - 2008. - № 3. - С. 53-55.
2. Carbon-based sliding materials. Schunk Kohlenstoffte-chnik GmbH, Germany, 2019. P. 22.
3. Sogabe T., Onishi Y., Inoue H., Okada O., Matsumoto T. Development of metal-impregnated carbon materials by using HIP.The Review of High Pressure Science and Technology. 1997. P. 1072-1074.
4. Луц, А. Р. Алюминиевые композиционные сплавы - сплавы будущего : Учебное пособие / А. Р. Луц, И. А. Галочкина. - Самара : Самар. гос. техн. ун-т, 2013. - 82 с.: ил.
5. Курбаткина, Е. И. Исследование влияния добавки кремния на фазовый состав алюминиевых композиционных материалов, армированных частицами карбида кремния / Е. И. Курбаткина, Д. В. Косолапов, Л. Г. Ходыкин, М. С. Нигметов // Авиационные материалы и технологии. - 2014. - № S6. - С. 35-38.