Interaction of the components in the Gd-Mn-Sn ternary system at 873 and 673 K

Abstract

The interaction of the components in the Gd-Mn-Sn ternary system was studied using the methods of X-ray and microstructure analyses, in the whole concentration range. The phase diagrams of the Gd-Mn-Sn system were constructed at 873 and 673 K. At both temperature of investigation the Gd-Mn-Sn system is characterized by existence of two ternary compounds: GdMn6Sn6 (MgFe6Ge6 structure type, space group P6/mmm) and Gd4Mn4Sn7 (Zr4Co4Ge7 structure type, space group I4/mmm). The formation of the interstitial solid solution GdMnхSn2 based on GdSn2 (ZrSi2-type) binary compound was found up to 10 at. % Mn at 873 K and 673 K. The existence of the substitutional solid solution based on GdMn2 (MgCu2-type) was observed up to 5 at.% Sn and 3 at. % Sn at 873 K and 673 K, respectively.