Bi-modal particle size distribution for high energy product hybrid Nd–Fe–B—Sm–Fe–N bonded magnets

Abstract

In this work, we have demonstrated high energy product bonded magnet by leveraging the variation in sizes between Nd-Fe-B and Sm-Fe-N, as well as their hard magnetic properties. The hybrid anisotropic bonded magnets contain 70 vol% of magnet powder (Dy-free Nd-Fe-B and Sm-Fe-N) and 30 vol% of nylon. The objective of the work was to create bi-modal and bi-compositional bonded magnets in which the fine (3μm) particles of Sm-Fe-N would be used to fill the voids between the bigger Nd-Fe-B (105μm) particles, thus improve packing density. The magnetic hysteresis loop did not show significant signs of decoupled interactions between the magnetic phases. It was also found that the performance of the bonded magnet was most enhanced at 1:4 ratio of Nd-Fe-B and Sm-Fe-N. At that ratio, maximum density of 5 g/cm3 and the highest (BH)max value of 18.5 MGOe were obtained, although the intrinsic coercivity decreased, relative to the trend seen for other ratios. This work advances the opportunity to expand the use of Sm-Fe-N in bonded magnet applications.