Strain rate induced toughening of individual collagen fibrils

Author:

Yang Fan1,Das Debashish1ORCID,Chasiotis Ioannis1ORCID

Affiliation:

1. Aerospace Engineering, University of Illinois at Urbana-Champaign, Urbana, Illinois 61801, USA

Abstract

The nonlinear mechanical behavior of individual nanoscale collagen fibrils is governed by molecular stretching and sliding that result in a viscous response, which is still not fully understood. Toward this goal, the in vitro mechanical behavior of individual reconstituted mammalian collagen fibrils was quantified in a broad range of strain-rates, spanning roughly six orders of magnitude, from 10−4 to 35 s−1. It is shown that the nonlinear mechanical response is strain rate sensitive with the tangent modulus in the linear deformation regime increasing monotonically from 214 ± 8 to 358 ± 11 MPa. More pronounced is the effect of the strain rate on the ultimate tensile strength that is found to increase monotonically by a factor of four, from 42 ± 6 to 160 ± 14 MPa. Importantly, fibril strengthening takes place without a reduction in ductility, which results in equivalently large increase in toughness with the increasing strain rate. This experimental strain rate dependent mechanical response is captured well by a structural constitutive model that incorporates the salient features of the collagen microstructure via a process of gradual recruitment of kinked tropocollagen molecules, thus giving rise to the initial “toe-heel” mechanical behavior, followed by molecular stretching and sustained intermolecular slip that is initiated at a strain rate dependent stress threshold. The model shows that the fraction of tropocollagen molecules undergoing straightening increases continuously during loading, whereas molecular sliding is initiated after a small fibril strain (1%–2%) and progressively increases with applied strain.

Funder

National Institutes of Health

Publisher

AIP Publishing

Subject

Physics and Astronomy (miscellaneous)

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3