Giant room temperature magnetocaloric response in a (MnNiSi)1−x(FeNiGa)x system

Abstract

The coincidence of magnetic and structural transitions near room temperature is observed in (MnNiSi)1− x(FeNiGa) x ( x = 0.16 and 0.17) systems, which leads to a coupled magnetostructural transition (MST) from a high-temperature paramagnetic Ni2In-type hexagonal phase to a low-temperature ferromagnetic TiNiSi-type orthorhombic phase associated with a substantial change in magnetization and a large change in structural unit cell volume, and thus, across MST, a giant magnetocaloric effect is obtained in these systems. The alloys with x = 0.16 and 0.17 are observed to show a giant isothermal magnetic entropy change (ΔSM) of about −26.2 and −63.2 J kg−1 K−1, accompanied with a large relative cooling power of about 220.1 and 264.5 J/kg, respectively, due to a magnetic field change ( μ0Δ H) of 5 T only. Moreover, the material with x = 0.16 and 0.17 shows a large temperature average magnetic entropy change of about −21.64 and −34.4 J kg−1 K−1 over a temperature span of 10 K due to μ0Δ H ∼ 5 T. Thus, these low-cost materials with giant magnetocaloric responses are highly suitable to be used as magnetic refrigerants for room temperature solid-state-based cooling technology.