Affiliation:
1. Department of Materials Science and Engineering, Texas A&M University 1 , College Station, Texas 77840, USA
2. Department of Materials Science and Engineering, University of California 2 , Irvine, California 92697, USA
3. Department of Metallurgical and Materials Engineering, University of Alabama 3 , Tuscaloosa, Alabama 35487, USA
4. Department of Materials Science and Engineering, University of Connecticut 4 , Storrs, Connecticut 06269, USA
5. J. Mike Walker ’66 Department of Mechanical Engineering, Texas A&M University 5 , College Station, Texas 77840, USA
Abstract
Bulk, polycrystalline (Co, Cu, Mg, Ni, Zn)O was synthesized using solid-state sintering. Micropillars were prepared and mechanically deformed along three crystallographic orientations: (001), (101), and (111). Pillars (001) and (111) cracked, while Pillar (101) remained intact. Pillars (001) and (101) exhibited activated slip systems, confirmed by a large stress drop, and the presence of slip bands, respectively. Schmid factor (SF) analysis was performed to examine the effect of grain orientations on dislocation activity and slip behavior. SF values range from 0 to 0.5, with non-zero values indicating potential for slip. Six slip systems exist in the (Co, Cu, Mg, Ni, Zn)O rock salt crystal structure: 1/2⟨110⟩11¯0. For the (001) orientation, four slip systems are potentially active (SF = 0.5). For the (101) orientation, there are four potentially active slip systems (SF = 0.25). For the (111) orientation, no potentially active slips systems exist (SF = 0). Dislocation structures, which were observed post-compression via transmission electron microscopy, demonstrated variations in size, number, and distribution across the pillar, depending on micropillar orientation. Entangled dislocations created misorientation in Pillar (001), which led to the possible formation of subgrains, while singular dislocations were observed in Pillar (101), and a lack of dislocations was observed in Pillar (111). Zener–Stroh type dislocation entanglement-mediated cracking is the proposed cause of the transgranular-type cracks in Pillar (001). The possible subgrain formation, or lack of formation, respectively, caused intergranular-type cracks to additionally form in Pillar (001), while Pillar (111) only exhibited transgranular-type brittle fracture. In combination, these findings highlight the importance of dislocation activity, without the need for elevated temperature, and grain orientation in controlling the mechanical deformation response in single-phase (Co, Cu, Mg, Ni, Zn)O.
Funder