Electromechanical properties of BS-PT ceramics under uniaxial pressure and hydrostatic pressure

Abstract

The increasing demands of device applications in harsh environments have led to higher expectations for temperature and pressure resistance in high-temperature piezoelectric materials. In order to understand the performance characteristics of BiScO3-PbTiO3 (BS-PT) high-temperature piezoelectric materials in practical device applications, this study focuses on analyzing the dielectric, piezoelectric, and ferroelectric properties of BS-64PT ceramics under uniaxial stress up to 150 MPa, as well as its electromechanical performance under a hydrostatic pressure of up to 400 MPa. As the uniaxial pressure increases, both the bias-field and large-signal piezoelectric coefficients exhibit a pattern of initially increasing and subsequently decreasing. Furthermore, the bias-field piezoelectric coefficient exceeds 450 pC/N and the large-signal piezoelectric coefficient surpasses 630 pC/N under uniaxial pressures below 100 MPa. This highlights their exceptional resistance to depolarization caused by uniaxial stress. To obtain more precise piezoelectric properties for BS-64PT ceramics in the 31 and 33 modes under hydrostatic pressure, the admittance fitting method was utilized. This method takes into account the significant losses at higher pressures. Within the pressure range of 0–400 MPa, the values of d33 and d31 for BS-64PT ceramics exhibited a minor change of 7.6% and 8%, respectively. These findings indicate that BS-64PT ceramics exhibit more stable piezoelectric properties under both uniaxial and hydrostatic pressures when compared to the majority of Pb-based perovskite-structured materials. The exceptional stability of piezoelectric properties in BS-PT ceramics can be primarily attributed to their elevated anisotropy energy or coercivity field compared to other perovskite-structured Pb(Mg1/3Nb2/3)O3 (PMN) / Pb(Zr,Ti)O3 (PZT)-based ceramics reported.