Influence of Potential Scan Rate on Corrosion Behaviour of Heat Treated AA 7075 Alloy in Sulphuric Acid Solution-Reference-Cited by-同舟云学术

Influence of Potential Scan Rate on Corrosion Behaviour of Heat Treated AA 7075 Alloy in Sulphuric Acid Solution

Published:2018-03-22 Issue:1 Volume:15 Page:91-99
ISSN:0973-3469
Container-title:Material Science Research India
language:
Short-container-title:Mat Sci Res India

Author:

Kumar Neeraj¹^ORCID,Manoj Manoranjan Kumar²,Phani M. Kalyan¹

Affiliation:

1. Department of Metallurgical and Materials Engineering, OP Jindal University, Raigarh, India.

2. Department of Metallurgical Engineering, National Institute of Technology, Raipur, India.

Abstract

In this paper, the effect of scan rate on the corrosion parameters and electrochemical behaviour of Retrogression and Re-aging (RRA) heat treatment of 7075 aluminium alloy has been investigated by Potentiodynamic polarization (PD) and electrochemical impedance spectroscopy (EIS) methods. The Potentiodynamic polarization (PD) curves were obtained at various scan rates for aged aluminium alloys in 0.5 M H2SO4 solution. The results show that at high scan rates shows unpredicted fluctuation of charging current, whereas at lower scan rates fewer disturbances are observed. The aged samples were chemically and mechanically characterized. It was observed that the RRA at 0.7 h shown improved corrosion property as well as mechanical properties compared to T6 temper. The corrosion properties were confirmed by EIS and polarization experiments.

Publisher

Oriental Scientific Publishing Company

Subject

Pharmacology (medical),Complementary and alternative medicine,Pharmaceutical Science

Reference22 articles.

1. 1. Chen J., Zhen L., Yang S., Shao W & Dai S., et al. Investigation of precipitation behavior and related hardening in AA 7055 aluminum alloy. Mat. Sci and Eng. A. 2009;500:34–42.

2. 2. Chun F., Zhi-yi L., Ai-lin N., Yan-bin Z. S. L., et al. Retrogression and re-aging treatment of Al-9.99%Zn-1.72%Cu-2.5%Mg-0.13%Zr aluminum alloy. Trans. of Non. 2006;1163–1170.

3. 3. Butler J. A. V., M. S., et al., A Kinetic Theory of Reversible Oxidation Potentials at Inert Electrodes. Trans. Faraday Soc. 1924;19;734–739.

4. 4. Krishnan A., Raja V. S & Mukhopadhyay A., et al. K. Influence of Retrogression and Re-aging on the Exfoliation Corrosion Behavior of AA 7085 Sheets. 2016;15(4):159–165.

5. 5. Kumar N., Manoj M. K & Haldar R., et al. Effect of Re-Aging on Strength , Corrosion and Dry Sliding Wear Behavior of 7075 Aluminum Alloy. J. Mater. Sci. Nanotechnol. 2016;4(2):1–8.

Cited by 11 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Evaluation of Healthcare Operations Management using TOPSIS Method;Journal on Innovations in Teaching and Learning;2024-07-31

2. Processes of Self‐Management Using Evaluation Based On Distance from Average Solution (EDAS);Journal on Innovations in Teaching and Learning;2024-07-31

3. Analysis of Child Safety Monitoring System using the SPSS Method;Journal on Innovations in Teaching and Learning;2024-07-31

4. The Company Law Analysis using the (COPRAS) Method;Journal on Innovations in Teaching and Learning;2024-07-31

5. An Overview of Qualitative Comparative Analysis Using GRA Methodology;Journal on Innovations in Teaching and Learning;2024-07-31