BACKGROUND: Radiation caries is a serious complication to head and neck cancer (HNC) radiotherapy, for which the primary teeth are more susceptible to be affected. Preventive protocols are recommended to enhance dental structure resistance against the direct effects of radiotherapy.
AIM: The aim of the study is to evaluate the effect of diode laser and two types of remineralizing agents on the microhardness of the primary teeth enamel and examine microstructural alterations.
METHODS: Twenty primary molars were sectioned into two halves in a mesiodistal direction, to obtain 40 specimens, which were then randomly allocated into five groups. Group 1 (Control Negative) n = 5 was not subjected to any treatment or radiation. Group 2 (Control positive) n = 5 was gamma irradiated with a dose of 60 Gray. For Groups 3, 4, and 5, specimens were divided into two subgroups: A and B (n = 5/subgroup). Subgroups A were gamma irradiated, then exposed to different surface treatments: 3A:10% nano-hydroxyapatite (nHA) paste, 4A: 5% sodium fluoride varnish (FV), and 5A: diode laser 980 nm. Subgroups B were exposed to surface treatments (3B: 10% nHA, 4 B: 5% FV, and 5B: diode laser 980 nm), then gamma irradiated. Surface micromorphology and microhardness were examined using environmental scanning electron microscope (ESEM), and Vickers microhardness tester, respectively.
RESULTS: Group 2 (G) specimens possessed the lowest mean microhardness, while nHA-G (3B), G-Fl (4A), and L-G (5B) had significantly higher values. ESEM analysis showed an alteration in Group G and the obliteration of enamel micropores with remineralizing agents. The melting and fusion of enamel in laser subgroups were also observed.
CONCLUSIONS: The findings indicated that using FV, nHA, or diode laser increased microhardness and maintained the integrity of the enamel microstructure. Therefore, applying preventive strategies should be considered in HNC radiotherapy.