Influence of shot peening and thermal aging treatment on resistance to intergranular corrosion in shielded metal arc weld metal for type 600 nickel base alloy-Reference-Cited by-同舟云学术

Influence of shot peening and thermal aging treatment on resistance to intergranular corrosion in shielded metal arc weld metal for type 600 nickel base alloy

Published:2015 Issue:2 Volume:33 Page:153-159
ISSN:0288-4771
Container-title:QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY
language:en
Short-container-title:QUARTERLY JOURNAL OF THE JAPAN WELDING SOCIETY

Author:

NISHIKAWA Satoru¹,OOI Koichi²,TAKAHASHI Makoto³,FURUKAWA Takashi¹

Affiliation:

1. Japan Power Engineering and Inspection Corporation

2. Shibaura Institute of Technology (Present Address: Nippon Welding Rod Co., LTD.)

3. Joining and Welding Research Institute, Osaka University

Publisher

Japan Welding Society

Subject

Metals and Alloys,Surfaces, Coatings and Films,Mechanical Engineering,Mechanics of Materials

Reference12 articles.

1. 1) T. Aoki, S. Hattori, H. Anzai and H. Sumimoto: Stress Corrosion Cracking In Ni-base Alloy Used for a Long Time in a BWR, Mentenology, 4-1 (2005), 34-41. (in Japanese)

2. 2) T. Fukumura and N. Totsuka: Primary Coolant Leakage Path Research of Reactor Vessel Head Penetration, Journal of the Institute of Nuclear Safety System, 15 (2008), 113-124. (in Japanese)

3. 3) N. Saito, S. Tanaka and H. Sakamoto: Effect of Corrosion Potential and Microstructure on the Stress Corrosion Cracking Susceptibility of Nickel-Base Alloys in High-Temperature Water, Corrosion, 59-12 (2003), 1064-1074.

4. 4) C. L. Briant and E. L. Hall: The Microstructural Causes of Intergranular Corrosion of Alloys 82 and 182, Corrosion, 43-9 (1987), 539-548.

5. 5) K. Yamauchi, I. Hamada, T. Okazaki and T. Yokono: Improvement of Intergranular Corrosion and Intergranular Stress Corrosion Cracking Resistance of Nickel-Base Weld Metals by Stabilization Parameter Control, Boshoku Gijyutsu, 35 (1986), 605-615. (in Japanese)