On the State of Graphene Oxide Nanosheet in a Polyurethane Matrix

Abstract

Mechanically strong and thermally stable films obtained from a water-based polyurethane (PU) dispersion with small (0.1–1.5 wt.%) additions of graphene oxide nanosheet (GO) were studied through elemental analysis, X-ray photoelectron spectroscopy, differential thermogravimetry, and Raman spectroscopy. Moreover, the depletion of near-surface layers in nitrogen was presented for all the samples under study. It was found that the introduction of GO into a PU matrix was ac-companied by a partial reduction of graphene oxide nanosheet and an increase in the concentra-tion of defects in its structure.