Characterization of Blend PA6 +EPDM (60/40) by Tensile Tests

Abstract

This paper presents a characterization of PA6 and the blend PA6+EPDM (60/40) by tensile tests in order to evaluate several mechanical properties for impact resistance applications. Results were found to be dependend on test rate (10 mm/min, 250 mm/min and 1000 mm/mm). SEM investigation point out a homogenous structure. The blend has better value of energy at break, for the higher test speed: for v=250 mm/min this characteristic has the value of energy at break 29.7 J and the blend has 76.3 J. At 1000 mm/min, PA6 has this charcateristic of 20 J, but for the blend, it is almost insensitive for the two higher test speeds (76.3 J at 250 mm/min and 72.4 J at 1000 mm/min, respectively) as compared to the neat polymer that decreases this feature when thr test spee increases. At the lowest teste speed, the values of energy at break for the materials in this study are close (90.2 J for PA6 and 87.7 J for the blend). The results from tensile tests pointed out that the formulated blend is recommended for impact resistance applications.