Author:
Shi Liang,Liu Cheng,Zhang Huaiwu
Abstract
As the main carrier for microwave circuits, microwave dielectric ceramics are receiving a lot of attention as the main carrier for the current 5G and pre-developed 6G communication technologies. A series of Nb5+ doped MgTa2O6 ceramics were synthesized by the solid-state reaction method X-ray diffraction confirmed that a single tetragonal structure can be formed when the doping amount is lower than 0.03, a heterogeneous structure of tetragonal and orthorhombic crystal structure is formed when the doping amount is lower than 0.15, and the tetragonal structure is completely transformed into orthorhombic structure when the doping exceeds 0.15. SEM results also show the transformation process of the grains of tetragonal structure to orthorhombic structure. The optimum microwave dielectric properties were obtained for 9% Nb5+ doped samples: εr = 24, Q×f = 71,000 GHz (at 8.9 GHz), TCF = 15 ppm/oC.
Publisher
Darcy & Roy Press Co. Ltd.
Reference13 articles.
1. I.M. Reaney, D. Iddles, Microwave Dielectric Ceramics for Resonators and Filters in Mobile, J. Am. Ceram. Soc., 89 (2006) 2063-2072.
2. H. Yang, S. Zhang, H. Yang, Y. Yuan, E. Li, Gd2Zr3(MoO4)9 microwave dielectric ceramics with trigonal structure for LTCC application, Journal of the American Ceramic Society, (2019).
3. B.J. Tao, C.F. Xing, W.F. Wang, H.T. Wu, Y.Y. Zhou, A novel Ce2Zr3(MoO4)9 microwave dielectric ceramic with ultra-low firing temperature, Ceram. Int., (2019).
4. W. Liu, R. Zuo, A novel low-temperature firable La2Zr3(MoO4)9 microwave dielectric ceramic, Journal of the European Ceramic Society, 38 (2018) 339-342.
5. Z. Jinjie, Y. Yaokang, W. Haitao, Y. Zhou, Z. Zhang, Structure, infrared spectra and microwave dielectric properties of the novel Eu2TiO5 ceramics, J. Am. Ceram. Soc., 103 (2020) 4333-4341.