Abstract
AbstractNanoparticle-reinforced metal matrix composite coatings have significant potential in mechanical part surface strengthening owing their excellent mechanical properties. This paper reports a phenomenon in which the grain orientation gradually evolves to (220) as the deposition current density increases when preparing nanoparticle-reinforced nickel-based composite coatings through jet electrodeposition (JED). During the preparation of the Ni-SiC composite coatings, the deposition current density increased from 180 A/dm2 to 220 A/dm2, and TC(220) gradually increase from 41.4% to 97.7%. With an increase of TC(220), the self-corrosion potential increases from −0.575 to −0.477 V, the corrosion current density decreases from 9.52 μA/cm2 to 2.76 μA/cm2, the diameter of the corrosion pits that after 10 days of immersion in a 3.5 wt% NaCl solution decreases from 278–944 nm to 153–260 nm, and the adhesion of the coating increases from 24.9 N to 61.6 N. Compared a conventional electrodeposition (CED), the Ni-SiC composite coating using JED has the advantages of a smooth surface morphology, high corrosion resistance, and strong adhesion, which are more obvious with an increase in TC(220).
Funder
National Natural Science Foundation of China
Publisher
Springer Science and Business Media LLC
Subject
Industrial and Manufacturing Engineering,Mechanical Engineering
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献