Author:
Lin Qiaoli,Liu Lu,Zhu Wenqi
Abstract
AbstractThe formation of a precursor film (PF) is always coupled with better wettability; thus, clarifying the formation mechanism is required to optimize the interfacial structures. However, recent research focuses on inert wetting systems at room temperature, which cannot guide practical material processing at high temperatures. In this review, PF formation mechanisms at high temperatures were reviewed. The mechanisms are surface diffusion, evaporation–condensation, subcutaneous infiltration, and rapid absorption and film overflow. In experimental metal/metal systems, the most probable mechanism is subcutaneous infiltration, related to the apparent contact angle, radius, and height of the gap between the substrate metal and the oxide film. The rapid absorption and film overflow mechanism usually occurs in metal/ceramic systems. The PF appearance for the adsorption mechanism must satisfy the paradox, that is, the relative inertial and high-affinity liquid/solid interface. Finally, another possible mechanism of PF appearance for the reactive wetting system at high temperatures was proposed, that is, the thin-surface transport mechanism. The PF formation is sensitive to external conditions. Therefore, it is necessary to develop thermodynamic and dynamic models for predicting and simulating PFs.
Funder
National Natural Science Foundation of China
Publisher
Springer Science and Business Media LLC
Subject
Industrial and Manufacturing Engineering,Mechanical Engineering
Reference72 articles.
1. T A Siewert, R W Heine, M G Lagally. Brazing alloy spreading on steel. Welding Journal, 1978, 57: 31-37.
2. B W Edmund, S G Gary, R H David. Precursor film controlled wetting of Pb on Cu. Physical Review Letters, 2003, 91(23) : 1-4.
3. G L J Bailey, H C Watkins. The flow of liquid metals on solid metal surfaces and its relation to soldering, brazing, and hot-dip coating. J Inst Metals, 1951, 80: 57-75.
4. W III Hardy. The spreading of fluids on glass. Philosophical Magazine and Journal of Science, 1919, 38(223): 49-55.
5. W Radigan, H Ghiradella, H L Frisch, et al. Kinetics of spreading of glass on fernico metal. Journal of Colloid and Interface Science, 1974, 49(2): 241-248.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献