Wear behaviour of hybrid (boron carbide-graphite) aluminium matrix composites under high temperature

Abstract

AbstractAluminium MMCs are among the many metal composites and are regarded as progressive engineering materials in numerous industries because of their advantages compared to standard aluminium alloy. Among the reinforcements in MMCs, ceramic particles are preferred for their superior wear resistance, temperature resistance, and adhesion to their matrix, making them a popular choice. This research work has been carried out to synthesise ceramic particle-reinforced aluminium metal matrix composites and to evaluate their tribological properties at different temperatures (50–300℃). Al2618 alloy was selected as the matrix, and boron carbide (B4C) and graphite (Gr) were selected as reinforcements. Hybrid composites are prepared through stir casting by varying the wt.% of B4C and Gr reinforcement particles with a ratio of 3:2. Microstructural observation shows the uniform distribution of B4C and Gr particles throughout the matrix without any agglomeration, and it also exhibits excellent scanning electron microscope (SEM). X-ray diffraction analysis (XRD) was performed to verify the presence of different constituents in the developed material. Samples S4 (Al 2618 + 12 wt.% B4C—8 wt.% Gr) and S5 (Al 2618 + 15 wt.% B4C—10 wt.% Gr) exhibit enhanced wear resistance (16.45%) due to the incorporation of a higher quantity of Gr solid lubricants alongside B4C within the temperature range of 50 to 300℃. The thickness and stability of the glazed layer exhibited adequate resistance to wear.