Abstract
Abstract
Background
High-translucency monolithic zirconia were developed to combine the esthetics of all ceramic restorations with the strength properties of zirconia. The purpose of this study was to compare the color stability of high-translucency monolithic zirconia ceramics with lithium disilicate luted using light-cure versus dual-cure resin cements following thermocyclic aging.
Methods
Forty specimens, each composed of 10 × 10 × 1 mm ceramic slice luted to dentin surface of an extracted tooth, were prepared and assigned into four groups (n = 10) as follows; LiDi/LC: lithium disilicate luted by light-cure resin cement; LiDi/DC: lithium disilicate luted by dual-cure resin cement; Zr/LC: zirconia luted by light-cure resin cement; and Zr/DC: zirconia luted by dual-cure resin cement. Color analysis of the specimens was performed before and after 3000 thermal cycles by means of spectrophotometry. The CIE L*a*b* values of the specimens were measured, and data were analyzed statistically at a significance value of p < 0.05.
Results
Thermocycling resulted in a significant change in color coordinates of specimens with an overall ΔE = 3.59 ± 1.60, but there was no statistically significant difference in the color change value among all tested groups (P = 0.756).
Conclusions
At 1 mm restoration thickness, the color stability of high-translucency monolithic lithium disilicate and zirconia ceramics were not significantly different irrespective of the cement type used.
Clinical implication Understanding the difference in color stability of dental ceramics may help in determining long-term esthetic result.
Publisher
Springer Science and Business Media LLC
Reference26 articles.
1. Zarone F, Ferrari M, Mangano FG, et al. “Digitally oriented materials”: focus on lithium disilicate ceramics. Int J Dent. 2016;2016:9840594.
2. Church TD, Jessup JP, Guillory VL, et al. Translucency and strength of high-translucency monolithic zirconium oxide materials. Gen Dent. 2017;65:48–52.
3. Yan J, Kaizer MR, Zhang Y. Load-bearing capacity of lithium disilicate and ultra-translucent zirconia. J Mech Behav Biomed Mater. 2018;88:170–5.
4. Putra A, Chung KH, Flinn BD, et al. Effect of hydrothermal treatment on light transmission of translucent zirconias. J Prosthet Dent. 2017;118:422–9.
5. Karaokutan I, Yilmaz-Savas T, Aykent F, et al. Color stability of CAD/CAM fabricated inlays after accelerated artificial aging. J Prosthodont. 2016;25:472–7.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献