The Prussian blue analogues represent well-known and extensively studied group of coordination species which has many remarkable applications due to their ion-exchange, electron transfer or magnetic properties. Among them, Co-Fe Prussian blue analogues have been extensively studied due to the photoinduced magnetization. Surprisingly, their suitability as precursors for solid-state synthesis of magnetic nanoparticles is almost unexplored.
In this paper, the mechanism of thermal decomposition of [Co(en)3][Fe(CN)6] ∙∙ 2H2O (1a) is elucidated, including the topotactic dehydration, valence and spins exchange mechanisms suggestion and the formation of a mixture of CoFe2O4-Co3O4 (3:1) as final products of thermal degradation.
Results
The course of thermal decomposition of 1a in air atmosphere up to 600°C was monitored by TG/DSC techniques, 57Fe Mössbauer and IR spectroscopy. As first, the topotactic dehydration of 1a to the hemihydrate [Co(en)3][Fe(CN)6] ∙∙ 1/2H2O (1b) occurred with preserving the single-crystal character as was confirmed by the X-ray diffraction analysis. The consequent thermal decomposition proceeded in further four stages including intermediates varying in valence and spin states of both transition metal ions in their structures, i.e. [FeII(en)2(μ-NC)CoIII(CN)4], FeIII(NH2CH2CH3)2(μ-NC)2CoII(CN)3] and FeIII[CoII(CN)5], which were suggested mainly from 57Fe Mössbauer, IR spectral and elemental analyses data. Thermal decomposition was completed at 400°C when superparamagnetic phases of CoFe2O4 and Co3O4 in the molar ratio of 3:1 were formed. During further temperature increase (450 and 600°C), the ongoing crystallization process gave a new ferromagnetic phase attributed to the CoFe2O4-Co3O4 nanocomposite particles. Their formation was confirmed by XRD and TEM analyses. In-field (5 K / 5 T) Mössbauer spectrum revealed canting of Fe(III) spin in almost fully inverse spinel structure of CoFe2O4.
Conclusions
It has been found that the thermal decomposition of [Co(en)3][Fe(CN)6] ∙∙ 2H2O in air atmosphere is a gradual multiple process accompanied by the formation of intermediates with different composition, stereochemistry, oxidation as well as spin states of both the central transition metals. The decomposition is finished above 400°C and the ongoing heating to 600°C results in the formation of CoFe2O4-Co3O4 nanocomposite particles as the final decomposition product.
Publisher
Springer Science and Business Media LLC
Reference86 articles.
1. Verdaguer M, Girolami GS, Miller JS, Drillon M: Magnetic Prussian Blue Analogs. Magnetism: Molecules to Materials, Volume 5. 2005, Weinheim: Wiley-VCH Verlag GmbH & Co. KGaA
2. Catala L, Volatron F, Brinzei D, Mallah T: Functional Coordination Nanoparticles. Inorg Chem. 2009, 48: 3360-3370. 10.1021/ic8012574.
3. Ricci F, Palleschi G: Sensor and biosensor preparation, optimisation and applications of Prussian Blue modified electrodes. Biosens Bioelectron. 2005, 21: 389-407. 10.1016/j.bios.2004.12.001.
4. Jayalakshmi M, Scholz FJ: Performance characteristics of zinc hexacyanoferrate/Prussian blue and copper hexacyanoferrate/Prussian blue solid state secondary cells. J Power Sources. 2000, 91 (2): 217-223. 10.1016/S0378-7753(00)00475-4.
5. Hu B, Fugetsu B, Yu H, Abe Y: Prussian blue caged in spongiform adsorbents using diatomite and carbon nanotubes for elimination of cesium. J Hazard Mater. 2012, 217–218: 85-91.
Cited by
21 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献