Abstract
AbstractThe adhesion of coatings on a given substrate has fundamental importance on a coating/substrate system's functionality. The current paper presents the adhesion strength results of FeCr and CoCr-based deposits produced by the electric arc thermal spray process on carbon steel, with an intermediate layer of 95Ni5Al. Three chemical compositions were tested for coating deposition and were characterized using plate and tube specimens made of carbon steel UNS G10200 to result in a screening of performance. Microstructural evaluation by optical microscopy (OM), scanning electron microscopy (SEM), and X-ray diffraction (XRD) were performed. Coating strength was measured using the standard pull-off test method. The corrosion resistance was analyzed with salt spray exposure, electrochemical polarization, and impedance spectroscopy (EIS) tests. The adhesion strength of FeCr and CoCr alloy coatings shows an overall average tensile strength of 27.2 MPa. All sealed conditions presented low corrosion and the samples with epoxy sealant exhibited a high resistance against corrosion. The X-ray diffraction results have revealed alpha and gamma FeCr alloys and chromite as deposited phases after the coating process.
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Polymers and Plastics,Surfaces, Coatings and Films,Dentistry (miscellaneous)
Reference30 articles.
1. Taheri K, Elhoriny M, Plachetta M, Gadow R. Thermodynamic analysis of resources used in thermal spray processes: energy and exergy methods. Entropy. 2016;18(7):237.
2. Hsu WL, Murakami H, Yeh JW, Yeh AC, Shimoda K. On the study of thermal-sprayed Ni0.2Co0.6Fe0.2CrSi0.2AlTi0.2HEA overlay coating. Surf Coat Technol. 2017;316:71–4.
3. Saravanan S, Ravichandran M, Balasubramaniyan V. Comparison studies on effect of thermal spray coating in internal combustion engine. MechMechEng. 2016;20(1):23–322.
4. Silva DP, Churiaque C, Bastos IN, Sánchez-Amaya JM. Tribocorrosion study of ordinary and laser-melted Ti6Al4V alloy. Metals. 2016;6(10):253.
5. Wielage B, Hofmann U, Steinhauser S, Zimmermann G. Improving wear and corrosion resistance of thermal sprayed coatings. Surf Eng. 1998;14(2):136–8.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献