Compressive Strength of Newly Developed Nonsintered Hydroxyapatite Blocks for Bone Graft Applications

Author:

Sunarso Sunarso1ORCID,Suryadi Abdi2,Indrani Decky Joesiana1,Pangesty Azizah Intan3

Affiliation:

1. Departement of Dental Materials Science, Faculty of Dentistry, Universitas Indonesia, Jakarta, Indonesia

2. Department of Dental Materials Science, Faculty of Dentistry, Universitas Indonesia, Jakarta, Indonesia

3. Department of Metallurgical and Materials Engineering, Faculty of Engineering, Universitas Indonesia, UI Campus, Depok, West Java, Indonesia

Abstract

Abstract Objective This study aimed to fabricate and evaluate the phase purity and compressive strength of the nonsintered hydroxyapatite (HA) block obtained via phase transformation of set calcium sulfate dihydrate (CSD) block under hydrothermal conditions at different temperatures. Materials and Methods Nonsintered HA block was prepared by immersion CSD block (4 mm in diameter and 8 mm in height) in a 1 mol/L sodium phosphate (Na3PO4) solution under hydrothermal conditions at 100°C, 140°C, and 180°C for 48 hours. X-ray diffraction was used to determine the crystalline phase of the obtained blocks. The mechanical strength of the blocks was measured using a compressive strength test. Results The result shows that the CSD block could be fully transformed into a HA block at 180°C for 48 hours without changing its macroscopic shape. The compressive strength of the obtained blocks was lower compared with the CSD block. Conclusion The current method has successfully produced a nonsintered HA block at 180°C for 48 hours. The compressive strength of the HA block decreased compared with the gypsum block used as a precursor. However, the compressive strength of the HA block that was produced still falls within the range of cancellous bone.

Publisher

Georg Thieme Verlag KG

Subject

General Dentistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3