Technical assessment of shear bond strength at ceramo-alloy interface after various surface treatment combinations and application of metal bonding agent

Abstract

BACKGROUND: Bonding between metal and ceramic is one of the most important aspects of a successful prosthesis. Various methods have been recommended for preparing the metal surface to enhance the bond between metal and ceramic including the use of a metal bonding agent. OBJECTIVE: This study aims to evaluate and compare the shear bond strength of the metal-ceramic (M-C) interface after combinations of various surface treatments including the application of a metal bonding agent. METHOD: 40 Ni-Cr alloy specimens were made and divided into 4 groups of 10 each based on the combination of surface treatments. Sandblasting, surface grinding, and Oxidation heat treatment (OHT) were performed on specimens from Group 1 (Control). In addition, Group 2 specimens received ultrasonic cleaning, Group 3 steam cleaning, and Group 4 metal bonding agent application. Following surface treatments on all specimens, porcelain build-up was performed, and shear bond strength was tested in a Digital Universal testing machine. The statistical tests used were independent t-test and ANOVA. RESULTS: Results revealed that Group 4 specimens had the highest mean value of shear bond strength of 39.087 MPa while Group 3 specimens showed the least mean shear bond strength of 18.154 MPa with highly statistically significant results (p< 0.001). CONCLUSION: The surface treatments and application of bonding agent to metal prior to porcelain application resulted in increased shear bond strength of the metal-ceramic interface.