Crack propagation and divergence phenomena observed by Caustics method in tempered glass-Reference-Cited by-同舟云学术

Crack propagation and divergence phenomena observed by Caustics method in tempered glass

Published:2021-04-27 Issue:4 Volume:13 Page:197-214
ISSN:1567-2069
Container-title:Strength, Fracture and Complexity
language:
Short-container-title:SFC

Author:

Aratani Shin’ichi¹

Affiliation:

1. , , , Japan E-mail: wildv4nn1@yahoo.co.jp

Abstract

High speed photography by Caustics method using Cranz-Schardin camera was studied for crack propagation and divergence in thermally tempered glass. Tempered 10 mm thick glass plates were used as a specimen. Two types of bifurcation and branching as the crack divergence could be observed and clarified even in 10 mm thick tempered glass. The difference of the shadow spot sizes between bifurcation type and branching type could be confirmed.

Publisher

IOS Press

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics

Reference21 articles.

1. Estimation of the 𝜎CR generated at propagating crack front in zone-tempered glass;Aratani;J. Ceram. Soc. Jpn.,2018

2. Crack divergence phenomena in tempered glass;Aratani;Strength, Fracture and Complexity,2020

3. Fracture of glass;Aratani;J. Jpn. Soc. Strength Frac. Mater.,2014

4. Dynamic fracture process of thermally tempered glass studied by the method of Caustics;Aratani;J. Ceram. Soc. Jpn., Int. Edition,1993

5. Generation of secondary cracks in tempered soda-lime-silica glass;Aratani;J. Ceram. Soc. Jpn.,1993

Cited by 2 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. New crack generation due to two-crack collision in 3.5 mm thick tempered glass;Strength, Fracture and Complexity;2023-06-09

2. New crack generation phenomena by crack collision in 10 mm thick tempered glass;Strength, Fracture and Complexity;2021-10-20