Abstract
This study aims to enhance the H2/N2 separation performance of polysulfone (PSF) hollow fiber membranes by annealing. X-ray diffraction, SEM, and FESEM were utilized to evaluate morphological and structural changes in denser annealed PSF membranes. AFM topography images were used to investigate the annealed form and roughness of PSF membranes. Before testing membrane permeation, it was annealed at 120, 150, and 190 °C to optimize gas separation performance. Compare to all annealing temperatures (120, 150, and 190 °C), the annealed PSF membrane at 150 °C had the greatest H2/N2 selectivity (16.18), but its separation performance was unsatisfactory since it was below the Robeson upper limit curve. The PSF before annealing and the PSF annealed at 190 °C showed outstanding separation performance (2.60 and 2.71, respectively), despite their lower selectivity than the PSF annealed at 150 °C
Publisher
Rasayan Journal of Chemistry
Subject
General Pharmacology, Toxicology and Pharmaceutics,General Energy,General Chemical Engineering,Biochemistry,General Chemistry
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献