Assessing the roles of mechanical cracks in Ni-rich layered cathodes in the capacity decay of liquid and solid-state batteries

Abstract

Mechanical cracks produced by mechanical pressure cause significant initial capacity loss but little capacity decay in subsequent cycles in ASSB. In contrast, in LELIBs mechanical cracks do not induce initial capacity loss but produce long lasting capacity decay during cycling.