Ballistic Behaviour of Austempered Compacted Graphite Iron Perforated Plates

Abstract

In this study, the performance of austempered compacted graphite iron was evaluated to find its suitability as perforated plates used in add-on armour. Perforated compacted graphite plates were subjected to austenitisation at 900 °C for 2 h followed by austempering at 275 and 400 °C for 1 h. The basic plate was fixed at 400 mm away from the perforated plate and armour and then piercing incendiary projectile was shot from a distance of 100 m. It was observed that both 7 mm and 9 mm perforated plates austempered at lower temperature of 275 °C producing higher hardness and lower ductility were effective in fracturing the penetrating core, thereby significantly decreasing the chances of penetrating the basic plate.