AbstractThe strength of materials depends on the rate at which they are tested, as defects, for example dislocations, that move in response to applied strains have intrinsic kinetic limitations1–4. As the deformation strain rate increases, more strengthening mechanisms become active and increase the strength4–7. However, the regime in which this transition happens has been difficult to access with traditional micromechanical strength measurements. Here, with microballistic impact testing at strain rates greater than 106 s−1, and without shock conflation, we show that the strength of copper increases by about 30% for a 157 °C increase in temperature, an effect also observed in pure titanium and gold. This effect is counterintuitive, as almost all materials soften when heated under normal conditions. This anomalous thermal strengthening across several pure metals is the result of a change in the controlling deformation mechanism from thermally activated strengthening to ballistic transport of dislocations, which experience drag through phonon interactions1,8–10. These results point to a pathway to better model and predict materials properties under various extreme strain rate conditions, from high-speed manufacturing operations11 to hypersonic transport12.
Publisher
Springer Science and Business Media LLC
Reference50 articles.
1. Kocks, U. F., Argon, A. S. & Ashby, M. F. Thermodynamics and kinetics of slip. Prog. Mater. Sci. 19, 1–291 (1975).
2. Ashby, M. F. A first report on deformation-mechanism maps. Acta Metall. 20, 887–897 (1972).
3. Zerilli, F. J. & Armstrong, R. W. Dislocation-mechanics-based constitutive relations for material dynamics calculations. J. Appl. Phys. 61, 1816–1825 (1987).
4. Sargent, P. M. & Ashby, M. F. The Presentation of High Strain-Rates on Deformation Mechanism Maps ADA128822 (Defense Technical Information Center, 1983).
5. Armstrong, R. W. & Li, Q. Dislocation mechanics of high-rate deformations. Metall. Mater. Trans. A 46, 4438–4453 (2015).
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献