Abstract
AbstractUnavoidable nonmetallic inclusions generated in the steelmaking process are fatal defects that often cause serious corrosion failure of steel, leading to catastrophic accidents and huge economic losses. Over the past decades, extensive efforts have been made to address this difficult issue, but none of them have succeeded. Here, we propose a strategy of wrapping deleterious inclusions with corrosion-resistant niobium armour (Z phase). After systematic theoretical screening, we introduce minor Nb into duplex stainless steels (DSSs) to form inclusion@Z core-shell structures, thus isolating the inclusions from corrosive environments. Additionally, both the Z phase and its surrounding matrix possess excellent corrosion resistance. Thus, this strategy effectively prevents corrosion caused by inclusions, thereby doubly improving the corrosion resistance of DSSs. Our strategy overcomes the long-standing problem of “corrosion failure caused by inclusions”, and it is verified as a universal technique in a series of DSSs and industrial production.
Publisher
Springer Science and Business Media LLC
Subject
General Physics and Astronomy,General Biochemistry, Genetics and Molecular Biology,General Chemistry,Multidisciplinary
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献