Abstract
AbstractThe onset of yielding and the related atomic-scale plastic flow behavior of bulk metallic glasses at room temperature have not been fully understood due to the difficulty in performing the atomic-scale plastic deformation experiments needed to gain direct insight into the underlying fundamental deformation mechanisms. Here we overcome these limitations by combining a unique sample preparation method with atomic force microscopy-based indentation, which allows study of the yield stress, onset of yielding, and atomic-scale plastic flow of a platinum-based bulk metallic glass in volumes containing as little as approximately 1000 atoms. Yield stresses markedly higher than in conventional nanoindentation testing were observed, surpassing predictions from current models that relate yield stress to tested volumes; subsequent flow was then established to be homogeneous without exhibiting collective shear localization or loading rate dependence. Overall, variations in glass properties due to fluctuations of free volume are found to be much smaller than previously suggested.
Funder
U.S. Department of Energy
National Science Foundation
Publisher
Springer Science and Business Media LLC
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献