Octahedral oxide glass network in ambient pressure neodymium titanate

Abstract

AbstractRare-earth titanates form very fragile liquids that can be made into glasses with useful optical properties. We investigate the atomic structure of 83TiO2-17Nd2O3 glass using pair distribution function (PDF) analysis of X-ray and neutron diffraction with double isotope substitutions for both Ti and Nd. Six total structure factors are analyzed (5 neutron + 1 X-ray) to obtain complementary sensitivities to O and Ti/Nd scattering, and an empirical potential structure refinement (EPSR) provides a structural model consistent with the experimental measurements. Glass density is estimated as 4.72(13) g cm−3, consistent with direct measurements. The EPSR model indicates nearest neighbor interactions for Ti-O at $$\overline{r}_{TiO}$$ r ¯ TiO  = 1.984(11) Å with coordination of $$n_{TiO}$$ n TiO  = 5.72(6) and for Nd-O at $$\overline{r}_{NdO}$$ r ¯ NdO  = 2.598(22) Å with coordination of $$n_{NdO}$$ n NdO  = 7.70(26), in reasonable agreement with neutron first order difference functions for Ti and Nd. The titanate glass network comprises a mixture of distorted Ti-O5 and Ti-O6 polyhedra connected via 71% corner-sharing and 23% edge-sharing. The O-Ti coordination environments include 15% nonbridging O-Ti1, 51% bridging O-Ti2, and 32% tricluster O-Ti3. This structure is highly unusual for oxide glasses melt-quenched at ambient pressure, as it consists of Ti-Ox predominantly in octahedral (with nearly no tetrahedral) coordination.