Synthesis and characterization of hydroxyapatite nanoparticles from calcium hydroxide fouled with gases evolved from smokestack of glass industry

Abstract

AbstractIn glass industry, the evolved gases and fumes from burning the gas fuel absorbed in calcium hydroxide to minimize the pollution of environment. After a period of time, the calcium hydroxide fouled with sulphate and carbonate as action of the absorbed SO3 and CO2 gases. Based on our interest to treatment the solid waste materials, this study intended to convert the obtained waste of calcium hydroxide fouled with gases to valuable products. Firstly, this waste was treated with water, caustic soda and acids. The results confirmed the conversion of waste to pure calcium sulfate by treatment with 6 v/v% sulfuric acid. Secondly, the obtained calcium sulfate was reacted with ammonium dihydrogen phosphate solution for preparation of calcium hydroxyapatite (HAp) nanoparticles. The produced HAp sample was characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM) and scanning electron microscopy (SEM), thermal gravimetric analysis (TGA) and N2 adsorption measurements. The obtained findings confirmed that the HAp can be produced after calcination at 700 °C, nanorods-like of sizes ranged from 11 to 15 nm and with main surface functional groups of hydroxyapatite. TGA and DTA data indicated that HAp is thermally stable up to 700 °C. Also, the obtained HAp has Ca/P molar ratio of 1.60 and exhibited high total surface area of 146 m2/g with mesoporous structure which make this material can be used in medical and water purification applications.