Abstract
AbstractIn this study, a core–shell magnetic metal organic framework (MOF) catalyst was introduced based on Fe3O4 magnetic nanoparticles (MNPs) and copper organic frameworks. In this catalyst, Fe3O4 MNPs have been coated with MOFs in which copper was the inorganic nodes and 1,3,5-benzenetricarboxylic acid was the organic linkers. Then, the core–shell structures and catalytic efficiency have been confirmed properly and completely with various analyses such as FT-IR, TEM, SEM, TEM mapping, SEM mapping, EDX, PXRD, TGA, ICP and VSM. The Cu moieties in MOF and shell structures can catalyze the synthesis of 1,2,3-triazole derivatives with good to excellent yields in the presence of water as a green solvent. Moreover, this catalyst showed the high reusability due to the super paramagnetic properties.
Publisher
Springer Science and Business Media LLC
Reference75 articles.
1. Teymoori, E., Davoodnia, A., Khojastehnezhad, A. & Hosseininasab, N. Nanomagnetic organic-inorganic hybrid (CuFe2O4@ Si-Imid-PMo): an efficient green catalyst for the Synthesis of 2, 4, 5-trisubstituted imidazoles. Iran. Chem. Commun. 7, 271–282 (2019).
2. Moeinpour, F. & Khojastehnezhad, A. Polyphosphoric acid supported on Ni0.5Zn0.5Fe2O4 nanoparticles as a magnetically-recoverable green catalyst for the synthesis of pyranopyrazoles. Arab. J. Chem. 10, 3468–3474 (2017).
3. Khojastehnezhad, A., Maleki, B., Karrabi, B. & Seresht, E. R. Synthesis of highly functionalized piperidines using polyphosphoric acid supported on silica-coated magnetic nanoparticles. Org. Prep. Proced. Int. 49, 338–345 (2017).
4. Hosseininasab, N., Davoodnia, A., Rostami-Charati, F. & Khojastehnezhad, A. Preparation, characterization, and first catalytic application of a novel phosphotungstic acid-containing ionic liquid immobilized on CuFe2O4@SiO2 magnetic nanoparticles in the synthesis of 1H-pyrazolo [1, 2-b] phthalazine-5, 10-diones. Russ. J. Gen. Chem. 87, 2436–2443 (2017).
5. Javid, A. et al. Synthesis of pyranopyrazoles using a magnetically separable modified preyssler heteropoly acid. Org. Prep. Proc. Int. 48, 377–384 (2016).