Abstract
AbstractThe magnetisation reversal behaviour as a function of composition was studied in low rare earth concentration alloys. 30 nm thick rare earth:transition-metal films of composition GdxCo100−x, GdxFe100−x and Gdx(Co50Fe50)100−x were prepared by magnetron sputtering, where x ranged from 4 to 13 atomic%. Magnetisation behaviour was studied using MOKE and Hall hysteresis measurements. The magnetic reversal behaviour as a function of Gd content is strongly dependent on the transition metal. With increasing Gd content the film structure transitions from crystalline to amorphous and the saturation magnetisation decreases linearly. For GdCo, the reversal field, Hc, increases by less than a factor of two with Gd doping of 11%, while for Fe, the coercivity falls by a factor of ten with 8% Gd. This may be attributed to changes in the crystalline morphology. GdCoFe shows a similar trend with Gd doping for the in-plane reversal field to that of GdFe. With 13% Gd in Fe there is evidence indicating the presence of a weak perpendicular magnetic anisotropy, PMA. With Gd doping the anomalous Hall resistivity of Co, Fe and CoFe increases significantly with the largest increase observed for GdCoFe.
Publisher
Springer Science and Business Media LLC
Cited by
10 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献