AbstractWe report the microstructure and thermoelectric properties of composite nanofiber webs, which were fabricated by dual-electrospinning of polyacrylonitrile (PAN) and sodium cobalt oxide (NaCo2O4) precursor solutions with different input compositions and following heat-treatment at 600–900 °C for simultaneous carbonation and calcination. The SEM and EDS mapping images revealed that PAN-derived carbon nanofibers (CNFs) and NaCo2O4-based ceramic nanofibers coexisted in the composite nanofiber webs and that their relative contents could be controlled by the input compositions. The Seebeck coefficient increased from ~26.77 to ~73.28 μV/K and from ~14.83 to ~40.56 μV/K with increasing the relative content of NaCo2O4 nanofibers in the composite nanofiber webs fabricated at 700 and 800 °C, respectively. On the other hand, the electrical conductivity of the composite nanofiber webs increased with the decrement of the relative content of NaCo2O4 nanofibers as well as the increment of the heat-treatment temperature. Owing to the opposite contributions of NaCo2O4 nanofibers and CNFs to the Seebeck coefficient, electrical conductivity and thermal conductivity, a maximum power factor of ~5.79 μW/mK2 and a figure of merit of ~0.01 were attained for CNF/NaCo2O4-based composite nanofiber webs fabricated at 45 wt% input composition of NaCo2O4 and at heat-treatment of 700 °C.
Publisher
Springer Science and Business Media LLC
Cited by
14 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献