Pitting Corrosion Mechanism of Alloy 800 in Simulated Crevice Chemistries Containing Thiosulfate

Published:2016 Issue:8 Volume:84 Page:585-596
ISSN:1344-3542
Container-title:Electrochemistry
language:en
Short-container-title:Electrochemistry

Author:

GAO Zhi-Ming¹,LU Xi-Bo¹,XIA Da-Hai¹²,YANG Li-Xia²,ZHU Ren-Kang³,BEHNAMIAN Yashar³

Affiliation:

1. Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engineering, Tianjin University

2. School of Material and Chemistry, China University of Geosciences

3. Department of Chemical and Materials Engineering, University of Alberta

Publisher

The Electrochemical Society of Japan

Subject

Electrochemistry

Link

https://www.jstage.jst.go.jp/article/electrochemistry/84/8/84_16-E00039/_pdf

Reference56 articles.

1. 1) R. W. Staehle and J. A. Gorman, Corrosion, 60, 115 (2004).

2. 2) L. Chi, G. Goszczynski, and Y. C. Lu, Test plan for investigating the low temperature degradation of steam generator tubing materials in the environments containing intermediate oxidation state of sulphur (OP-09-4076), Atomic Energy of Canada Ltd. p. 31 (2009).

3. 3) D.-H. Xia, R.-K. Zhu, Y. Behnamian, J.-L. Luo, C.-J. Lin, and S. Klimas, J. Electroanal. Chem., 744, 77 (2015).

4. 4) H.-S. Kuo, H. Chang, and W.-T. Tsai, Corros. Sci., 41, 669 (1999).

5. 5) E. A. Ashour, E. A. Abd El Meguid, and B. G. Ateya, Corrosion, 53, 612 (1997).

Cited by 8 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. A high-resolution characterization of surface film formed on alloys 800 and 690 exposed to chloride and thiosulfate-containing solution at 300°C;Anti-Corrosion Methods and Materials;2024-05-06

2. Crevice corrosion behaviors of Alloy 690 and 405 stainless steel in chloride solutions with different concentrations of thiosulfate;Journal of Nuclear Materials;2023-03

3. Insitu electrochemical impedance spectroscopy of PT-7 M and Fe-Ni-Cr alloys in chloride containing ammonia medium at high temperatures;Corrosion Science;2023-03

4. Pitting corrosion of Ni-Cr-Fe alloys at open circuit potential in chloride plus thiosulfate solutions;Corrosion Science;2022-04

5. Effect of Flow Rate on Corrosion Behavior and Hydrogen Evolution Potential of X65 Steel in 3.5% NaCl Solution;International Journal of Electrochemical Science;2019-03