Abstract
The absorption spectra of eight type I and three type II
a
diamonds irradiated with neutrons, electrons or y-rays have been recorded at 80 and 290°K after various heat treatments in the temperature range 0 to 900°C. It is found that heating in the range 350 to 450°C causes a general reduction in the irradiation-induced absorption owing to the recombination of those interstitials and vacancies which are near neighbours. Heating type II
a
diamonds at 600°C causes a large reduction in the irradiation-induced lines and new lines appear. These are probably due to pairs of identical defects, and the kinetics of their formation during isothermal heating at 600°C are presented. At higher temperatures all absorption lines in type II
a
diamonds disappear and only continuous absorption remains. This is probably due to amorphous or graphitic regions produced by agglomeration of defects. Type I diamonds show the same kind of absorption, but in addition show an increase in strength of the natural lines and also some new absorption lines which are not removed by heating at 900°C. It is suggested that these additional processes are due to the anchoring of vacant atomic sites and interstitial carbon atoms at crystal imperfections present only in type I diamonds.
Reference5 articles.
1. Proc. Roy;Clark C. D .;Soc. A,1956
2. Brit;Dugdale R .;J. Appl. Phys.,1953
3. Radiation-Induced Amorphism in Diamond
4. Reversible Bleaching of a Band in the Absorption Spectrum of Diamond
5. Z;Pringsheim P.;Phys.,1952
Cited by
122 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献