Final Irrigant Temoporfin, Femtosecond Laser, and Chitosan Nanoparticles on Extrusion Bond Strength of Glass Fiber Post, Microhardness, and Modulus of Elasticity of Canal Dentin

Abstract

Final root canal disinfectants Temoporfin, Femtosecond (FS) laser, and Chitosan nanoparticles (NPs) on marten hardness (MH), modulus of elasticity (EIT), and push-out bond strength (PBS) of glass fiber reinforced post (GFRP) to the root dentin. Sixty caries-free single-rooted human premolars were decoronated and a root canal was performed followed by post space. The specimens were then arbitrarily allocated into groups according to the final disinfectant used. Group 1: 17% EDTA, Group 2: Temoporfin, Group 3: FS laser and Group 4: Chitosan NPs. Evaluation of mechanical properties (MH and EIT) was performed on five samples from each group. Ten samples from each group were bonded with GFRP and sectioned. A universal testing machine and stereomicroscope were used to analyze the PBS and failure mode. Means and standard deviations (SD) of MH, EiT, and PBS were assessed using ANOVA and post hoc Tukey. The highest values of MH and EiT were revealed by 5.25% NaOCl+Chitosan NP samples. The lowest scores of MH and EiT were presented by samples irrigated with 5.25% NaOCl+17% EDTA. The coronal section of samples treated with 5.25% NaOCl+Chitosan NPs showed the highest EBS. Chitosan NPs and FS laser have proved to be valuable alternatives to EDTA as both improved PBS without deteriorating the MH and EiT.