Abstract
In this paper, mechanical properties (Young’s modulus and indentation hardness) were measured for three samples of healthy human enamel and dentin using nanoindentation in order to compare their mechanical characteristics. Each sample was a longitudinal section obtained from one maxillary molar, which was subjected to 60-second exposure in citric acid with different concentrations (0.5 wt.%, 3 wt.%, 5 wt.%). The Nanotest 600 Platform 3 nanoindentometer was used to test the samples. Load-displacement curves for both enamel and dentin were obtained for each of the three sections. As a result of experiments, a number of characteristic curves of the dependence of the indentation depth on the applied force (load—displacement curves) were constructed for each of the three slices. The dependence of changes in the mechanical properties (reduced Young’s modulus, indentation hardness) of human tooth enamel on the concentration of citric acid applied to the tooth surface has been established: an increase in the concentration of citric acid leads to a decrease in Young’s modulus and indentation hardness. No such correlation was found for dentin in this study.
Publisher
Stomatology for All - International Dental Review
Reference6 articles.
1. Tay F. Modern adhesive systems. Dent Art. 2003, №2: 13-16.
2. Kuznetsova E.D. Application of modern adhesive systems in clinical dentistry. A young scientist. 2019, №44(282): 143—147.
3. Scheffel D.L., Tenuta L.M., Cury J.A., Hebling J. Effect of acid etching time on demineralization of primary and permanent coronal dentin. Am J Dent. 2012, 25(4): 235—238.
4. Helvey G.A. Adhesive dentistry: the development of immediate dentin sealing/selective etching bonding technique. Compendium of continuing education in dentistry (Jamesburg, NJ: 1995). 2011), 32(9): 22—24.
5. Oliver W.C., Pharr G.M. An improved technique for determining hardness and elastic modulus using load and displacement sensing indentation experiments. J. Mater. Res. 1992, 7: 1564—1583.