Diametral tensile strength and water sorption of glass-ionomer cements used in Atraumatic Restorative Treatment

Abstract

The purposes of this study were to evaluate the diametral tensile strength and the water sorption of restorative (Fuji IX and Ketac Molar) and resin-modified glass-ionomer luting cements (ProTec Cem, Fuji Plus and Vitremer) mixed at both manufacturer and increased powder: liquid ratio, for their use in the Atraumatic Restorative Treatment. A conventional restorative glass-ionomer (Ketac Fil) was used as control. Specimens (6.0 mm in diameter x 3.0 mm in height) were prepared and stored (1 hour, 1 day and 1 week) for a diametral tensile strength test. Data were subjected to two-way ANOVA and Tukey tests (p<0.05). For the water sorption test, specimens of 15.0 mm in diameter x 0.5 mm in height were prepared and transfered to desiccators until a constant mass was obtained. Then the specimens were immersed in deionized water for 7 days, weighed and reconditioned to a constant mass in desiccators. Data were subjected to one-way ANOVA and Tukey tests (p<0.05). Five specimens of each studied material and consistency were prepared for each test. The resin-modified glass-ionomer cements showed significantly higher strength than the conventional materials. Except for ProTec Cem, the diametral tensile strength of the resin-modified materials significantly increased from luting to restorative consistency. Except for ProTec Cem, the water sorption of the resin-modified glass ionomers was higher than the others. The water sorption of resin-modified materials at restorative consistency was significantly lower than at luting consistency. Resin-modified glass-ionomer luting cements mixed at increased powder: liquid ratio showed better properties than at luting consistency.