Observations of Corrosion Product Formation and Stress Corrosion Cracking on Brass Samples Exposed to Ammonia Environments-Reference-Cited by-同舟云学术

Observations of Corrosion Product Formation and Stress Corrosion Cracking on Brass Samples Exposed to Ammonia Environments

Published:2019 Issue:1 Volume:22 Page:
ISSN:1980-5373
Container-title:Materials Research
language:
Short-container-title:Mat. Res.

Author:

Davalos-Monteiro Raul¹^ORCID

Affiliation:

1. The University of Manchester, United Kingdom

Publisher

FapUNIFESP (SciELO)

Subject

Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science

Link

http://www.scielo.br/pdf/mr/v22n1/1516-1439-mr-22-01-e20180077.pdf

Reference16 articles.

1. Electrochemistry of Stress Corrosion Cracking of Brass;Seleet MS,1986

2. The effects of corrosion rate and manufacturing in the prevention of stress corrosion cracking on structural members of steel bridges;Nugent M;The Journal of Corrosion Science and Engineering,2014

3. Copper and Copper Alloys;Davis JR,2001

4. Copper and Copper Alloys;Davis JR,2001

5. The correspondence between susceptibility to SCC of brass and corrosion-induced tensile stress with various pH values;Guo XJ;Corrosion Science,2002

Cited by 19 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Position-dependent degradation and damage mechanisms of Inconel 600 in an ammonia gas flow environment at elevated temperatures;Corrosion Science;2024-11

2. Comprehensive corrosion failure analysis of HAl77-2 alloy tubes serving in a low temperature multi-effect distillation plant: From feature analysis to corrosion mechanisms;Engineering Failure Analysis;2024-09

3. Stress corrosion cracking behaviors of carbon steel in liquid ammonia;Materials Research Express;2024-08-01

4. Stress corrosion cracking of leaded brass used in oil temperature sensor of vehicle;Engineering Failure Analysis;2024-04

5. Comprehensive Corrosion Failure Analysis of Hal77-2 Alloy Tubes Serving in a Low Temperature Multi-Effect Distillation Plant: From Feature Analysis to Corrosion Mechanisms;2024