Effect of calcium hydroxide intracanal dressing on the bond strength of a resin-based endodontic sealer

Author:

Barbizam João Vicente Baroni1,Trope Martin2,Teixeira Érica C.N.2,Tanomaru-Filho Mário3,Teixeira Fabrício B.2

Affiliation:

1. University of North Carolina, USA; State University of São Paulo, Brazil; University of Passo Fundo, Brazil

2. University of North Carolina, USA

3. State University of São Paulo, Brazil

Abstract

The aim of this in vitro study was to evaluate the bond strength of Epiphany™ resin-based sealer to dentin walls after placement of calcium hydroxide [Ca(OH)2] dressings. Fifteen extracted single-rooted human teeth were instrumented using 2.5% NaOCl + EDTA as irrigants. The teeth were randomly assigned to 3 groups (n=5), according to the intracanal dressing: G1= Ca(OH)2 + saline; G2= Ca(OH)2 + 2% chlorhexidine gluconate (CHX) gel; and G3= saline (control). After 10 days of storage in 100% humidity at 37ºC, the dressings were removed and the root canals were filled with Epiphany™ sealer. After additional 48 h of storage, the specimens were sectioned transversally into 2-mm-thick discs. Push-out tests were performed (1 mm/min, Instron 4411) and the maximum loads at failure were recorded in MPa. One-way ANOVA and Newman-Keuls tests showed a statistically significant decrease in bond strength when a Ca(OH)2 dressing was used before root canal filling with Epiphany™ (G1= 10.18 ± 1.99 and G2= 9.98 ± 2.97) compared to the control group (13.82 ± 3.9) (p< 0.05). It may be concluded that the use of Ca(OH)2 as an intracanal dressing material affected the adhesion of Epiphany™ to the root canal walls, but even though the values were within the acceptable range found in the literature.

Publisher

FapUNIFESP (SciELO)

Subject

General Dentistry

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3