Affiliation:
1. São Paulo State University, Brazil
Abstract
This study evaluated the effect of denture base polymer type (heat- and microwave-polymerized), ridge lap surface treatment (with and without methyl methacrylate-MMA etching) and thermocycling on the microtensile bond strength (µTBS) of Biotone acrylic teeth. Flat-ground, ridge-lap surface of posterior artificial teeth were bonded to cylinders of each denture base resin, resulting in the following groups (n=6): G1a - Clássico/with MMA etching; G1b - Clássico/without MMA etching; G2a - OndaCryl/with MMA etching; G2b - OndaCryl/without MMA etching. Rectangular bar specimens with a cross-sectional area of 1 mm² were prepared. Half of the bars in each group were thermocycled (5,000 cycles between 4ºC and 60ºC). µTBS testing was performed in an universal testing machine at a crosshead speed of 0.5 mm/min. Data were analyzed statistically by three-way ANOVA (α=0.05). There was no statisticaly significant difference (p>0.05) for the factors (resin, surface treatment,and thermocycling) or their interactions. The mean µTBS values (MPa) and standard deviations were as follows: Thermocycling - G1a: 41.00 (14.00); G1b: 31.00 (17.00); G2a: 50.00 (27.00); G2b: 40.00 (18.00); No thermocycling - G1a: 37.00 (14.00); G1b: 43.00 (25.00); G2a: 43.00 (14.00); G2b: 40.00 (27.00). The µTBS of Biotone artificial teeth to the denture base acrylic resins was not influenced by the polymer type, surface treatment or thermocycling.
Reference20 articles.
1. Shock absorbability and hardness of commercially available denture teeth;Kawano F;Int J Prosthodont,2002
2. The implant-supported overdenture as an alternative to the complete mandibular denture;Doundoulakis JH;J Am Dent Assoc,2003
3. Bonding acrylic teeth to acrylic resin denture bases: a review;Patil SB;Gerodontology,2006
4. Bond strength of acrylic teeth to denture base resin after various surface conditioning methods before and after thermocycling;Saavedra G;Int J Prosthodont,2007
5. Denture fracture: a survey;Darbar UR;Br Dent J,1994