Artificial teeth: evaluation of wear resistance, microhardness and composition

Abstract

Objective: To evaluate the Knoop hardness, composition, and wear resistance of acrylic-resin artificial teeth exposed to mechanical toothbrushing. Methods: Artificial teeth from three commercial brands - Biotone, Trilux, and Soluut PX - were used. From each brand, 10 teeth were selected for wear evaluation after mechanical brushing, 10 for microhardness testing, and 5 for composition analysis. Specimens underwent 55,000 brushing cycles, under a 200-g load and at a frequency of 250 cycles per minute, using a soft-bristled toothbrush (IndicatorPlus 30, Oral-B) soaked in a 1:1 toothpaste/water slurry (Oral B Pró Saúde). Microhardness testing was performed using a 25-g load for 15 seconds in an HMV-2 hardness tester (Shimadzu). The composition of teeth from different brands was determined by scanning electron microscopy with energy-dispersive X-ray spectroscopy (SEM/EDS) (Jeol JSM 5800). Results: Wear results after mechanical brushing were compared by means of the paired t-test, whereas those obtained in microhardness testing were compared by ANOVA with Bonferroni correction. There was no statistically significant difference between brands in either trial. Conclusion: Composition analysis revealed that all of the artificial teeth analyzed contain carbon and oxygen. Trilux and Soluut PX brand teeth also contain silicon; however, the presence of filler particles did not result in increased resistance.