Author:
Kauk Marit,Altosaar Mare,Raudoja Jaan,Timmo Kristi,Grossberg Maarja,Varema Tiit,Mellikov Enn
Abstract
AbstractCuInSe2 monograin powders (MGP) were synthesized from Cu-In alloys of different Cu/In concentration ratios and elemental Se in liquid phase of flux material in evacuated quartz ampoules. The surface morphology, phase structure, and composition of the powder crystals were analyzed by scanning electron microscopy, X-ray diffraction, and energy-dispersive X-ray analysis respectively. Bulk composition was analyzed polarographically. Photoluminescence spectra were measured at 9 K. It was found that the composition of MGP material (Cu/In concentration ratio) can be controlled by the concentration ratio of precursor Cu-In alloys. Single phase CuInSe2 growth is realisable between 0.7<Cu/In<1 at the growth temperature of 1000 K. Photoluminescence spectra of near-stoichiometric materials had one dominant peak at 0.93 eV, which is typical to In-rich CuInSe2. Samples with high In content exhibited two broad bands with peak positions at 0.86 and 0.93 eV.
Publisher
Springer Science and Business Media LLC
Reference12 articles.
1. Phase segregation, Cu migration and junction formation in Cu(In, Ga)Se2
2. Optical characterisation of high-quality CuInSe2 thin films synthesised by two-stage selenisation process
3. The η-phase field of the CuIn system
4. Electronic properties versus composition of thin films of CuInSe2
5. 2 Altosaar M. , Danilson M. , Kauk M. , Krustok J. , Mellikov E. , Raudoja J. , Timmo K. , Varema T. , Solar Energy Materials & Solar Cells, In Press, Corrected Proof, Dec. (2004)
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献