Wang C. A.,Turner G. W.,Manfra M. J.,Choi H. K.,Spears D. L.
Abstract
ABSTRACTGai1−xInxASySb1-y (0.06 < x < 0.18, 0.05 < y < 0.14) epilayers were grown lattice-matched to GaSb substrates by low-pressure organometallic vapor phase epitaxy (OMVPE) using triethylgallium, trimethylindium, tertiarybutylarsine, and trimethylantimony. These epilayers have a mirror-like surface morphology, and exhibit room temperature photoluminescence (PL) with peak emission wavelengths (λP,300K) out to 2.4 μm. 4K PL spectra have a full width at half-maximum of 11 meV or less for λP,4K < 2.1 μm (λP,300K = 2.3 μm). Nominally undoped layers are p-type with typical 300K hole concentration of 9 × 1015 cm−3 and mobility ∼ 450 to 580 cm2/V-s for layers grown at 575°C. Doping studies are reported for the first time for GalnAsSb layers doped n type with diethyltellurium and p type with dimethylzinc. Test diodes of p-GalnAsSb/n-GaSb have an ideality factor that ranges from 1.1 to 1.3. A comparison of electrical, optical, and structural properties of epilayers grown by molecular beam epitaxy indicates OMVPE-grown layers are of comparable quality.
Publisher
Springer Science and Business Media LLC
Reference16 articles.
1. Unstable Region in Quaternary In1-xGaxAs1-ySbyCalculated Using Strictly Regular Solution Approximation
2. 16. Charache G.W. , Egley J.L. , Danielson L.R. , DePoy D.M. , Baldasaro P.F. , Campbell B.C. , Hui S. , Frass L.M. , and Wojtczuk S.J. , presented at the 26th Photovoltaic Specialist Conf.
3. Growth characteristics of a vertical rotating-disk OMVPE reactor
4. 12. Wang C.A. , Salim S. , Jensen K.F. , and Jones A.C. , J. Cryst. Growth to be published.
Cited by
4 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献