Author:
Endo A.,Chauhan H. S.,Egi T.,Shiohara Y.
Abstract
Macrosegregation of Y2Ba1Cu1O5 (Y211) particles was observed in Pt-added Y1Ba2Cu3O7−δ (Y123) crystals grown by an undercooling method. It was found that the macrosegregation of Y211 particles depended on the growth direction and the growth rate (R) as a function of undercooling (ΔT). The amount of Y211 particles in Y123 crystals grown at large R was larger than at small R. Also, the amount of Y211 in Y123 growing along the a-direction was larger than that along the c-direction. Further, it was noted that the smaller Y211 particles in size were distributed in Y123 grown at large R. These phenomena could be at least qualitatively explained by the prevalent trapping/pushing theory. In the direct observation of magnetic flux with the Faraday effect of iron garnet film, the flux pinning force was found to be in good agreement with the macrosegregation of Y211 particles.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference33 articles.
1. Direct observation of magnetic flux behavior in high-Tc YBa2Cu30x superconductors using the magneto-optical effect of iron garnet films
2. 13. Cima M.J. , Rigby K. , Flemings M.C. , Haggerty J. S. , Homjo S. , Shen H. , and Sung T.H. , Extended Abstracts—Int. Workshop on Superconductivity, Maui, Hawaii (1995), p. 55.
3. Crystal chemistry and phase equilibria studies of theBaO(BaCO3)R2O3CuOsystems. IV. Crystal chemistry and subsolidus phase relationship studies of the CuO-rich region of the ternary diagrams,R =lanthanides
4. Semisolid solidification of high temperature superconducting oxides
5. Nonuniform distribution of second phase particles in melt-textured Y–Ba–Cu–O oxide with metal oxide (CeO2, SnO2, and ZrO2) addition
Cited by
177 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献