Al2O3 fiber strength degradation in metal and intermetallic matrix composites

Abstract

The mechanisms for fiber damage in single crystal Al2O3 fiber-reinforced composites were investigated. Both fiber fragmentation and fiber strength degradation were observed in composites with a variety of matrix compositions. Four mechanisms that may be contributing to the fiber strength loss have been proposed and include matrix reaction, reaction with binders, residual stress-induced damage, and pressure from hot pressing. The effect of matrix reaction was separated from the other three effects by sputter-coating the matrices on cleaned fibers and annealing with a temperature profile that simulates processing conditions. These experiments revealed that Y and Cr in FeCrAlY base alloys and Zr in NiAl alloys reacted with the fiber, and grooves and adherent particles were formed on the fiber surface which were responsible for the strength loss. The effects of the matrix reaction appeared to dominate over the other possible mechanisms, although evidence for reaction with binders was also found. Ridges on the fiber surface, which reflected the grain boundaries of the matrix, were also observed. In order for single-crystal Al2O3 to be used as a fiber in MMC's and IMC's, a matrix or protective coating which minimizes matrix reaction during processing will be necessary. Of the matrices investigated, the Thermo-spanTM alloy was the least damaging to fiber properties.