Surface Energy Driven Crystallization of Amorphous Pd81si19

Abstract

ABSTRACTIn-situ TEM investigations during thermal treatment of amorphous Pd81Si19 have been performed. It was found that crystalline nuclei are formed near the perforation edge of the hole produced by electrochemical polishing. After impinging with neighboring crystals, a crystallization front formed which was aligned parallel to the perforation edge. The crystallization front moved in the direction perpendicular to the perforation edge. Crystal growth was found to proceed faster in thinner parts of the specimen than in thicker parts. The results are described qualitatively within a thermodynamic model taking into account volume-, surface- and interfacial free energies and an appropriate specimen geometry.