Crystalline Morphologies of Polychloroprene Thin Films as Revealed by Transmission Electron Microscopy Observation

Abstract

Thin films of polychloroprene (CR; Neoprene-W) were made by casting its solution (2.0 wt%) in benzene onto the water surface, and some of them were stretched by a desired amount of strain (ε) in their “molten” state. The specimens thus prepared were then crystallized and examined by transmission electron microscopy. Morphological observations in bright- and dark-field imaging modes and selected-area electron diffraction analysis revealed directly that filamentous entities observed in the bright-field image are the edge-on lamellar crystals. It was, therefore, confirmed that the morphological results obtained from the thin specimens of CR without any electron staining are basically in accord with those reported so far for the OsO4-stained thin films of CR.